MIPA CX3 2K HS Express Klarlack Air Drying Clear Coat

• Colour shade transparent
• Mixing ratio 1 : 1 by volume
• Hardener 2K-HS-Härter HX 25 Dilution ready for spraying after hardener addition
• Spraying viscosity 20° C 14 - 16 s 4 mm DIN
• Spraying pressure 2 - 3 bar
• Spraying nozzle 1,0 -1.2 mm
• Spraying operations 2 coats
• Pot life approx. 30 minutes
• Coat thickness / dry film 40 - 50 μm
• Curing time / Flash off time 5 - 7 min. between the spraying operations
• Drying Object temperature 20 °C
  - dust dry: 10 15 min
  - set to touch: 30 - 45 min
  - ready for assembly: 60 min
  - ready for polishing: 60 min
• Drying Object temperature 60 °C
  - dust dry: 5 min.
  - set to touch: 15 min
  - ready for assembly: 15 min
  - ready for polishing: 15 min
• IR-Drying
  - flash off time: 7 - 10 min.
  - shortwave: 8 min.
  - mediumwave: 12 - 14 min.

Recommendations:

Attention: pot life and through hardening depend on air humidity conditions. Maskings and adhesive tapes, which has been recoated with Mipa-Express-Klarlack CX 3, have to be removed immediately after application process. Otherwise, the fresh lacquer will be peeled off with the adhesive tape. To use Mipa 2K-HS-Express-Klarlack CX3, 2K-hardeners must be added to two-coat basecoats. The mixing ratios are: Mipa BC + 10 % (10:1) Mipa 2K-HX 25. In particular, it is to be expected that the addition of hardener may cause a slight, systeminherent colour deviation when using bright metallic colours. Therefore it is improper to paint edge to edge. Blending by fading out the basecoat and spot repair application will avoid this negative effect. This product, as a system characteristic, may cause eye and skin irritation. Wear appropriate protective equipments. To coat deformable plastic parts, Mipa 2K-HS-Express-Klarlack CX 3 must be plastified with up to 15 % Mipa 2K-Elastic. In this case the drying time can be slightly longer