High quality protection for the bottom and visible body parts of vehicles.
Product Features
- Process with UBC Spray Gun
- Sprayable with all paint systems
- Permanently elastic
- Very good adhesion
- Weather resistant
- Resistant to weak acids and bases
- Excellent corrosion prevention
- Silencing
Description
The FINIXA Anti-Gravel Coating is based on synthetic resins and rubbers. This coating is quickly-drying and especially developed for a long-term gravel protection of front and rear spoilers, sills, side skirts, wheel arches, etc. The products are thixotropic and can be applied drip-free. The products have a good adhesion and can be painted over with any kind of lacquer system when the film is completely dried. Drying can take place at room temperature or at elevated temperatures up to 60°C. After application the result will be a closed, elastic and structured film with excellent rust- and gravel protection. FINIXA Anti-Gravel Coating also reduces the noise inside cars because of the sound dampening/proofing properties.
Application
Surface must be clean, rust-free and dry. Shake the can well before use. Application pressure = 3-5 bar. Recommended thickness = approximately 1 mm at application. For excellent corrosion protection bare metal should be treated with an anti corrosion primer prior to the use of AGB 01 – AGG01. Before over painting allow the coating to be completely dried.
Important:
Do not spray on the exhaust, brake systems, or on motor parts. After use, thoroughly rinse the pistol with solvent. Do not block the air valve at the base or the nozzle of the spraying gun. Clogged guns can cause can to explode.
Removement
FINIXA Anti-Gravel Coatingbe removed with aromatic solvents as white spirit, boiling point naphtha, xylene, etc.
Technical information:
- Base: Synthetic resins and rubbers, pigments and fillers.
- Color: Grey and Black
- Odour: Solvent
- Drying time: (20 º C) (1000 mu webt) 16 hours
- Recommended operating temperature range, º C : -30 to 95
- Peak temperature, º C : 110
- Density (20 º C), g/ml 1,05
- Solids 45 %